• To improve and stabilize the service life of hot - forging die fabricated by cast die steer , the failure modes and mechanism were analyzed
  摘要为了稳定和提高精铸热锻的使用寿命，研究了其失效形式和机理。
• Improper material composition and processing can cause earlier fracture failure and short life happened to the hot - forging dies
  不恰当的材质及工艺导致热锻模具出现早期断裂失效，失效形式不合理，寿命较低。
• Forging die is the most suitable for high speed milling application , because of its high hardness i material and lower surface roughness
  而各式模具中又以?模最为适合，因其模具材料硬度较高且模穴表面粗度要求较低。
• Abstract : in the paper , the hot crack for the forging die made by methodsof squeeze casting is analyzed , how to reduce the hot crack is also given out
  文摘:从生产实际出发，分析了锻模液态模锻成形过程中热裂纹形成的主要原因，提出了降低锻模热裂纹的几点措施。
• Traditional forging die manufacturing including a lot of process and using eom to form the impression results some disadvantages such as longer production time and higher cost
  摘要常规锻模加工，由于加工道次多，且需采用放电加工制造模穴，导致有制造时间长，且成本偏高的缺点。
• Traditional forging die manufacturing including a lot of process and using eom to form the impression results some disadvantages such as longer production time and higher cost
  摘要传统锻模加工，由于加工道次多，且需采用放电加工制造模穴，导致有制造时间长，且成本偏高的缺点。
• In order to apply this technology in practice , special development of cad ( computer aided design ) for the blade precision forging die is systematically studied on the basis of ugii ( v . 14 ) in this thesis
  本文针对这一迫切需要，利用ugii （ 14版）软件作为二次开发平台，对叶片精锻模cad二次开发作了系统的研究。
• Abstract : in the light of two common failure modes in use , i . e . thermal wear and hot fatigue crack , this paper analyzes the reasons and puts forward the measures to be taken for improving the life of forging die
  文摘:针对锻模在使用过程中常见的两种失效形式，即热磨损和热疲劳裂纹，分析了其产生的原因，并提出了为提高锻模寿命而应采取的措施。
• According to the structure of the final forging die , the flash groove is studied and coded into a separate sub - function . in order to split the upper and under dies , a sheet body of the separating surface is coded into a sub - function
  根据锻模设计要求，研究了分模面、毛边槽的设计并编制了相应模块；研究了锻模参数的计算和锻模实体的生成。
• This article introduces some general characteristics of magnesium alloys especially in forging , hoping to assist local forgers in realizing magnesium forging characteristics and forging die design guidelines so as to shorten the lead time of developing competitive magnesium forging components
  本文针对镁合金之锻造技术作一介绍，期能协助有兴趣之锻造业者，了解镁合金之锻造特性与锻造模具设计要领，进而早日开发出具竞争力之镁合金锻件。
• Upon technology analysis of series 350 crankshaft forging pieces of chevroler , proper forging technology has been designed adn forging die been optimized , resulting in high quality crankshaft forging pieces with high accuracy , good appearance and reasonable streamline , produced in model kp8000t crankshaft production line
  摘要通过对雪佛莱350系列曲轴锻件的工艺分析，设计了合理的锻造工艺方案，优化设计了锻模，在kp8000曲轴生产线上锻造出了精度高、外观质量好、流线合理的优质曲轴锻件。
• Column setup : die & mould technology overview ; cad / cam ; stamping die technology ; cavity die ( plastic die , die casting die , forging die , rubber model die , etc . ) technology ; die making technology ; die material and heat treatment technology ; business operation and management ; business information ; die & mould technology both here and abroad and lecture , etc
  主要栏目设置：模具技术综述、模具cad / cam 、冲模技术、型腔模（塑料模、压铸模、锻模、橡胶模等）技术、模具制造技术、模具材料及热处理技术、企业经营管理、行业信息、国内外模具技术及讲座等等。